 Phosphorus up to 0.10 per cent does not harm, and probably improves, irons containing silicon not above 0.15, and carbon not above 0.03. None of the ingredients except carbon in the proportions present seem to very notably affect welding by ordinary methods.  Transactions - Stran 124avtor: American Institute of Mining, Metallurgical, and Petroleum Engineers, American Institute of Mining Engineers - 1879Celotni ogled - O knjigi
 | United States. Board for testing iron, steel and other metals - 1878 - 842 strani
...Phosphorus up to 0.10 per cent, does not harm and probably improves irous containing silicon not alx>ve 0.15 and carbon not above 0.03. None of the ingredients,...and its welding power by ordinary methods are varied more by the amount of its reduction in rolling than by its ordinary differences in composition. Uniform... | |
 | United States. Board for testing iron, steel and other metals - 1878 - 862 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent, does not harm and probably improves irons...silicon not .above 0.15 and carbon not above 0.03. Xone of the ingredients, except carbon, in the proportions present, seem to very notably aft'ect welding... | |
 | Board for Testing Iron, Steel and Other Metals - 1878 - 318 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per •cent, does not harm and probably improves irons...silicon not above 0.15 and carbon not above 0.03. Xone of the ingredients, except •carbon, in the proportions present, seem to very notably affect... | |
 | 1878 - 568 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0-20 per cent. does not harm, and probably improves, irons containing silicon not above 0-15 and carbon not above 0-04. None of the ingredients, except carbon, in the proportions present,... | |
 | Lester Anthony Beardslee - 1879 - 142 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent does not harm, and probably improves, irons...affect welding by ordinary methods. II. The strength of wrought-iron and its welding power by ordinary methods are varied more by the amount of its reduction... | |
 | Lester Anthony Beardslee - 1879 - 140 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent does not harm, and probably improves, irons...affect welding by ordinary methods. II. The strength of wrought-iron and its welding power by ordinary methods are varied more by the amount of its reduction... | |
 | United States. Board for Testing Iron, Steel, and Other Metals - 1881 - 802 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent, does not harm and probably improves irons...carbon, in the proportions present, seem to very notably aflect welding by ordinary methods. II. The strength of wrought iron and its welding power by ordinary... | |
 | United States. Board for Testing Iron, Steel, and Other Metals - 1881 - 808 strani
...and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent, docs not harm and probably improves irons containing silicon...carbon, in the proportions present, seem to very notably aflect welding by ordinary methods. II. The strength of wrought iron and its welding power by ordinary... | |
 | United States. Board for testing iron, steel and other metals - 1881 - 804 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to 0.10 per cent, does not harm and probably improves irons containing silicon not above 0.15 aud carbon not above 0.03. None of the ingredients, except carbon, in the proportions present, seem... | |
 | Robert Henry Thurston - 1883 - 796 strani
...of phosphorus and silicon can be traced, and that of carbon is very obvious. Phosphorus up to o.io per cent. does not harm, and probably improves, irons containing silicon not above o. 1 5 and carbon not above 0.03. None of the ingredients, except carbon, in the proportions present,... | |
| |